EN 1.4841 Stainless Steel vs. ASTM Grade HN Steel

Both EN 1.4841 stainless steel and ASTM grade HN steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is ASTM grade HN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 32
9.0
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 650
500

Thermal Properties

Latent Heat of Fusion, J/g 330
310
Maximum Temperature: Corrosion, °C 440
420
Maximum Temperature: Mechanical, °C 1150
1080
Melting Completion (Liquidus), °C 1380
1400
Melting Onset (Solidus), °C 1340
1350
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Base Metal Price, % relative 25
26
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.3
4.6
Embodied Energy, MJ/kg 62
66
Embodied Water, L/kg 190
180

Common Calculations

PREN (Pitting Resistance) 26
22
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
17
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 4.0
3.5
Thermal Shock Resistance, points 15
11

Alloy Composition

Carbon (C), % 0 to 0.2
0.2 to 0.5
Chromium (Cr), % 24 to 26
19 to 23
Iron (Fe), % 47.1 to 55.5
44.9 to 57.8
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 19 to 22
23 to 27
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 1.5 to 2.5
0 to 2.0
Sulfur (S), % 0 to 0.015
0 to 0.040