EN 1.4841 Stainless Steel vs. EN 1.0406 Steel

Both EN 1.4841 stainless steel and EN 1.0406 steel are iron alloys. They have 53% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is EN 1.0406 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 32
23
Fatigue Strength, MPa 200
170
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 430
300
Tensile Strength: Ultimate (UTS), MPa 650
470
Tensile Strength: Yield (Proof), MPa 260
240

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1150
400
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
49
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.4
Embodied Energy, MJ/kg 62
19
Embodied Water, L/kg 190
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
89
Resilience: Unit (Modulus of Resilience), kJ/m3 170
150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0 to 0.2
0.22 to 0.29
Chromium (Cr), % 24 to 26
0 to 0.4
Iron (Fe), % 47.1 to 55.5
97.6 to 99.38
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 19 to 22
0 to 0.4
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 1.5 to 2.5
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.045