EN 1.4841 Stainless Steel vs. EN 1.4558 Stainless Steel

Both EN 1.4841 stainless steel and EN 1.4558 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is EN 1.4558 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 32
39
Fatigue Strength, MPa 200
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 430
350
Tensile Strength: Ultimate (UTS), MPa 650
510
Tensile Strength: Yield (Proof), MPa 260
200

Thermal Properties

Latent Heat of Fusion, J/g 330
300
Maximum Temperature: Corrosion, °C 440
480
Maximum Temperature: Mechanical, °C 1150
1100
Melting Completion (Liquidus), °C 1380
1400
Melting Onset (Solidus), °C 1340
1350
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 25
31
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 4.3
5.5
Embodied Energy, MJ/kg 62
77
Embodied Water, L/kg 190
200

Common Calculations

PREN (Pitting Resistance) 26
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
160
Resilience: Unit (Modulus of Resilience), kJ/m3 170
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 4.0
3.1
Thermal Shock Resistance, points 15
12

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.45
Carbon (C), % 0 to 0.2
0 to 0.030
Chromium (Cr), % 24 to 26
20 to 23
Iron (Fe), % 47.1 to 55.5
39.2 to 47.9
Manganese (Mn), % 0 to 2.0
0 to 1.0
Nickel (Ni), % 19 to 22
32 to 35
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 1.5 to 2.5
0 to 0.7
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
0 to 0.6