EN 1.4841 Stainless Steel vs. EN 1.4837 Stainless Steel

Both EN 1.4841 stainless steel and EN 1.4837 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is EN 1.4837 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 32
6.8
Fatigue Strength, MPa 200
120
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 650
500
Tensile Strength: Yield (Proof), MPa 260
250

Thermal Properties

Latent Heat of Fusion, J/g 330
320
Maximum Temperature: Corrosion, °C 440
440
Maximum Temperature: Mechanical, °C 1150
1050
Melting Completion (Liquidus), °C 1380
1390
Melting Onset (Solidus), °C 1340
1350
Specific Heat Capacity, J/kg-K 490
490
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
20
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
3.7
Embodied Energy, MJ/kg 62
53
Embodied Water, L/kg 190
180

Common Calculations

PREN (Pitting Resistance) 26
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
29
Resilience: Unit (Modulus of Resilience), kJ/m3 170
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 4.0
3.7
Thermal Shock Resistance, points 15
11

Alloy Composition

Carbon (C), % 0 to 0.2
0.3 to 0.5
Chromium (Cr), % 24 to 26
24 to 27
Iron (Fe), % 47.1 to 55.5
53.4 to 63.7
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 19 to 22
11 to 14
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 1.5 to 2.5
1.0 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.030