EN 1.4841 Stainless Steel vs. SAE-AISI 1043 Steel

Both EN 1.4841 stainless steel and SAE-AISI 1043 steel are iron alloys. They have 52% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is SAE-AISI 1043 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190 to 200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 32
13 to 18
Fatigue Strength, MPa 200
230 to 390
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 430
400 to 430
Tensile Strength: Ultimate (UTS), MPa 650
650 to 710
Tensile Strength: Yield (Proof), MPa 260
350 to 600

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1150
400
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 25
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.4
Embodied Energy, MJ/kg 62
18
Embodied Water, L/kg 190
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
87 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 170
320 to 980
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
23 to 25
Strength to Weight: Bending, points 21
21 to 22
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 15
21 to 22

Alloy Composition

Carbon (C), % 0 to 0.2
0.4 to 0.47
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 47.1 to 55.5
98.4 to 98.9
Manganese (Mn), % 0 to 2.0
0.7 to 1.0
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 1.5 to 2.5
0
Sulfur (S), % 0 to 0.015
0 to 0.050