EN 1.4841 Stainless Steel vs. SAE-AISI D3 Steel

Both EN 1.4841 stainless steel and SAE-AISI D3 steel are iron alloys. They have 64% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is SAE-AISI D3 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 32
9.8 to 15
Fatigue Strength, MPa 200
310 to 940
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
74
Shear Strength, MPa 430
470 to 1220
Tensile Strength: Ultimate (UTS), MPa 650
770 to 2050
Tensile Strength: Yield (Proof), MPa 260
480 to 1550

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1380
1430
Melting Onset (Solidus), °C 1340
1390
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 15
31
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
8.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
3.2
Embodied Energy, MJ/kg 62
48
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 26
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
97 to 180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
28 to 74
Strength to Weight: Bending, points 21
24 to 47
Thermal Diffusivity, mm2/s 4.0
8.3
Thermal Shock Resistance, points 15
23 to 63

Alloy Composition

Carbon (C), % 0 to 0.2
2.0 to 2.4
Chromium (Cr), % 24 to 26
11 to 13.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 47.1 to 55.5
80.3 to 87
Manganese (Mn), % 0 to 2.0
0 to 0.6
Nickel (Ni), % 19 to 22
0 to 0.3
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 1.5 to 2.5
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0
0 to 1.0
Vanadium (V), % 0
0 to 1.0