EN 1.4841 Stainless Steel vs. SAE-AISI H12 Steel

Both EN 1.4841 stainless steel and SAE-AISI H12 steel are iron alloys. They have 58% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is SAE-AISI H12 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
75
Tensile Strength: Ultimate (UTS), MPa 650
690 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1380
1480
Melting Onset (Solidus), °C 1340
1440
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
36
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
8.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.3
2.9
Embodied Energy, MJ/kg 62
41
Embodied Water, L/kg 190
76

Common Calculations

PREN (Pitting Resistance) 26
12
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
24 to 65
Strength to Weight: Bending, points 21
22 to 42
Thermal Diffusivity, mm2/s 4.0
9.8
Thermal Shock Resistance, points 15
22 to 60

Alloy Composition

Carbon (C), % 0 to 0.2
0.3 to 0.4
Chromium (Cr), % 24 to 26
4.8 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 47.1 to 55.5
87.8 to 91.7
Manganese (Mn), % 0 to 2.0
0.2 to 0.5
Molybdenum (Mo), % 0
1.3 to 1.8
Nickel (Ni), % 19 to 22
0 to 0.3
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 1.5 to 2.5
0.8 to 1.2
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0
1.0 to 1.7
Vanadium (V), % 0
0 to 0.5