EN 1.4841 Stainless Steel vs. S35125 Stainless Steel

Both EN 1.4841 stainless steel and S35125 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is S35125 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 32
39
Fatigue Strength, MPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Shear Strength, MPa 430
370
Tensile Strength: Ultimate (UTS), MPa 650
540
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 330
300
Maximum Temperature: Corrosion, °C 440
490
Maximum Temperature: Mechanical, °C 1150
1100
Melting Completion (Liquidus), °C 1380
1430
Melting Onset (Solidus), °C 1340
1380
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 25
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 4.3
6.4
Embodied Energy, MJ/kg 62
89
Embodied Water, L/kg 190
210

Common Calculations

PREN (Pitting Resistance) 26
30
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
170
Resilience: Unit (Modulus of Resilience), kJ/m3 170
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
19
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 4.0
3.1
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.1
Chromium (Cr), % 24 to 26
20 to 23
Iron (Fe), % 47.1 to 55.5
36.2 to 45.8
Manganese (Mn), % 0 to 2.0
1.0 to 1.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 19 to 22
31 to 35
Niobium (Nb), % 0
0.25 to 0.6
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 1.5 to 2.5
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.015