EN 1.4848 Stainless Steel vs. R30075 Cobalt

EN 1.4848 stainless steel belongs to the iron alloys classification, while R30075 cobalt belongs to the cobalt alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4848 stainless steel and the bottom bar is R30075 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210 to 250
Elongation at Break, % 9.0
12
Fatigue Strength, MPa 130
250 to 840
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
82 to 98
Tensile Strength: Ultimate (UTS), MPa 510
780 to 1280
Tensile Strength: Yield (Proof), MPa 250
480 to 840

Thermal Properties

Latent Heat of Fusion, J/g 320
320
Melting Completion (Liquidus), °C 1390
1360
Melting Onset (Solidus), °C 1340
1290
Specific Heat Capacity, J/kg-K 490
450
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.1

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 4.4
8.1
Embodied Energy, MJ/kg 63
110
Embodied Water, L/kg 200
530

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 38
84 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 150
560 to 1410
Stiffness to Weight: Axial, points 14
14 to 17
Stiffness to Weight: Bending, points 25
24 to 25
Strength to Weight: Axial, points 18
26 to 42
Strength to Weight: Bending, points 18
22 to 31
Thermal Diffusivity, mm2/s 3.9
3.5
Thermal Shock Resistance, points 11
21 to 29

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Boron (B), % 0
0 to 0.010
Carbon (C), % 0.3 to 0.5
0 to 0.35
Chromium (Cr), % 24 to 27
27 to 30
Cobalt (Co), % 0
58.7 to 68
Iron (Fe), % 45.4 to 55.7
0 to 0.75
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
5.0 to 7.0
Nickel (Ni), % 19 to 22
0 to 0.5
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.1
Tungsten (W), % 0
0 to 0.2