EN 1.4859 Stainless Steel vs. AISI 202 Stainless Steel

Both EN 1.4859 stainless steel and AISI 202 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4859 stainless steel and the bottom bar is AISI 202 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
210 to 300
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
14 to 45
Fatigue Strength, MPa 140
290 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 490
700 to 980
Tensile Strength: Yield (Proof), MPa 210
310 to 580

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 560
410
Maximum Temperature: Mechanical, °C 1050
910
Melting Completion (Liquidus), °C 1410
1400
Melting Onset (Solidus), °C 1360
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 36
13
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.2
2.8
Embodied Energy, MJ/kg 88
40
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 21
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
120 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 110
250 to 840
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
25 to 35
Strength to Weight: Bending, points 17
23 to 29
Thermal Diffusivity, mm2/s 3.4
4.0
Thermal Shock Resistance, points 11
15 to 21

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.15
Chromium (Cr), % 19 to 21
17 to 19
Iron (Fe), % 40.3 to 49
63.5 to 71.5
Manganese (Mn), % 0 to 2.0
7.5 to 10
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 31 to 33
4.0 to 6.0
Niobium (Nb), % 0.5 to 1.5
0
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.060
Silicon (Si), % 0.5 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030