EN 1.4859 Stainless Steel vs. ASTM A227 Spring Steel

Both EN 1.4859 stainless steel and ASTM A227 spring steel are iron alloys. They have 46% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4859 stainless steel and the bottom bar is ASTM A227 spring steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
500 to 640
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
12
Fatigue Strength, MPa 140
900 to 1160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 490
1720 to 2220
Tensile Strength: Yield (Proof), MPa 210
1430 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
400
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 36
1.8
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.2
1.4
Embodied Energy, MJ/kg 88
19
Embodied Water, L/kg 190
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
200 to 260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
61 to 79
Strength to Weight: Bending, points 17
41 to 48
Thermal Diffusivity, mm2/s 3.4
14
Thermal Shock Resistance, points 11
55 to 71

Alloy Composition

Carbon (C), % 0.050 to 0.15
0.45 to 0.85
Chromium (Cr), % 19 to 21
0
Iron (Fe), % 40.3 to 49
97.4 to 99.1
Manganese (Mn), % 0 to 2.0
0.3 to 1.3
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 31 to 33
0
Niobium (Nb), % 0.5 to 1.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0.5 to 1.5
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.050