EN 1.4859 Stainless Steel vs. EN 1.4319 Stainless Steel

Both EN 1.4859 stainless steel and EN 1.4319 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4859 stainless steel and the bottom bar is EN 1.4319 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
51
Fatigue Strength, MPa 140
240
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 490
640
Tensile Strength: Yield (Proof), MPa 210
250

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 560
410
Maximum Temperature: Mechanical, °C 1050
890
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1360
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 36
13
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.2
2.7
Embodied Energy, MJ/kg 88
39
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 21
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
260
Resilience: Unit (Modulus of Resilience), kJ/m3 110
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 17
21
Thermal Diffusivity, mm2/s 3.4
4.0
Thermal Shock Resistance, points 11
14

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.070
Chromium (Cr), % 19 to 21
16 to 18
Iron (Fe), % 40.3 to 49
70.8 to 78
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 31 to 33
6.0 to 8.0
Niobium (Nb), % 0.5 to 1.5
0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0.5 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030