EN 1.4859 Stainless Steel vs. EN 1.5515 Steel

Both EN 1.4859 stainless steel and EN 1.5515 steel are iron alloys. They have 46% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4859 stainless steel and the bottom bar is EN 1.5515 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
150 to 170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 490
490 to 1760

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
48
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 36
1.9
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.2
1.4
Embodied Energy, MJ/kg 88
19
Embodied Water, L/kg 190
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
17 to 63
Strength to Weight: Bending, points 17
18 to 41
Thermal Diffusivity, mm2/s 3.4
13
Thermal Shock Resistance, points 11
14 to 52

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.050 to 0.15
0.35 to 0.4
Chromium (Cr), % 19 to 21
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 40.3 to 49
97.8 to 98.9
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 31 to 33
0
Niobium (Nb), % 0.5 to 1.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0.5 to 1.5
0.15 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025