EN 1.4859 Stainless Steel vs. EN 1.5637 Steel

Both EN 1.4859 stainless steel and EN 1.5637 steel are iron alloys. They have 49% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4859 stainless steel and the bottom bar is EN 1.5637 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
24
Fatigue Strength, MPa 140
280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 490
560
Tensile Strength: Yield (Proof), MPa 210
390

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
410
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 36
4.0
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 6.2
1.8
Embodied Energy, MJ/kg 88
24
Embodied Water, L/kg 190
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
120
Resilience: Unit (Modulus of Resilience), kJ/m3 110
410
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 3.4
14
Thermal Shock Resistance, points 11
16

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.15
Chromium (Cr), % 19 to 21
0
Iron (Fe), % 40.3 to 49
94.9 to 96.5
Manganese (Mn), % 0 to 2.0
0.3 to 0.8
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 31 to 33
3.3 to 3.8
Niobium (Nb), % 0.5 to 1.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0.5 to 1.5
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.0050
Vanadium (V), % 0
0 to 0.050