EN 1.4903 Stainless Steel vs. ASTM A732 Cast Steel

Both EN 1.4903 stainless steel and ASTM A732 cast steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4903 stainless steel and the bottom bar is ASTM A732 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20 to 21
4.0 to 25
Fatigue Strength, MPa 320 to 330
230 to 750
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
72 to 73
Tensile Strength: Ultimate (UTS), MPa 670 to 680
460 to 1470
Tensile Strength: Yield (Proof), MPa 500
310 to 1340

Thermal Properties

Latent Heat of Fusion, J/g 270
250 to 260
Maximum Temperature: Mechanical, °C 650
400 to 430
Melting Completion (Liquidus), °C 1460
1440 to 1460
Melting Onset (Solidus), °C 1420
1400 to 1420
Specific Heat Capacity, J/kg-K 470
470 to 480
Thermal Conductivity, W/m-K 26
39 to 50
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.4
7.1 to 7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 4.0
8.2 to 8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
2.0 to 3.8
Density, g/cm3 7.8
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 2.6
1.4 to 1.7
Embodied Energy, MJ/kg 36
19 to 24
Embodied Water, L/kg 88
47 to 54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 130
45 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 650
260 to 4770
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
16 to 52
Strength to Weight: Bending, points 22
17 to 37
Thermal Diffusivity, mm2/s 7.0
10 to 14
Thermal Shock Resistance, points 23
14 to 43