EN 1.4911 Stainless Steel vs. SAE-AISI A9 Steel

Both EN 1.4911 stainless steel and SAE-AISI A9 steel are iron alloys. They have 87% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4911 stainless steel and the bottom bar is SAE-AISI A9 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
74
Tensile Strength: Ultimate (UTS), MPa 1070
770 to 2030

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 20
35
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
9.2

Otherwise Unclassified Properties

Base Metal Price, % relative 20
7.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.4
4.7
Embodied Energy, MJ/kg 49
70
Embodied Water, L/kg 130
82

Common Calculations

PREN (Pitting Resistance) 14
10
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 38
28 to 73
Strength to Weight: Bending, points 30
24 to 46
Thermal Diffusivity, mm2/s 5.4
9.6
Thermal Shock Resistance, points 37
25 to 66

Alloy Composition

Boron (B), % 0.0050 to 0.015
0
Carbon (C), % 0.050 to 0.12
0.45 to 0.55
Chromium (Cr), % 9.8 to 11.2
4.8 to 5.5
Cobalt (Co), % 5.0 to 7.0
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 75.7 to 83.8
87 to 90.5
Manganese (Mn), % 0.3 to 1.3
0 to 0.5
Molybdenum (Mo), % 0.5 to 1.0
1.3 to 1.8
Nickel (Ni), % 0.2 to 1.2
1.3 to 1.8
Niobium (Nb), % 0.2 to 0.5
0
Nitrogen (N), % 0 to 0.035
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0.1 to 0.8
1.0 to 1.2
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0 to 0.7
0
Vanadium (V), % 0.1 to 0.4
0.8 to 1.4