EN 1.4913 Stainless Steel vs. C61500 Bronze
EN 1.4913 stainless steel belongs to the iron alloys classification, while C61500 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4913 stainless steel and the bottom bar is C61500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 14 to 22 | |
| 3.0 to 55 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 75 | |
| 42 |
| Shear Strength, MPa | 550 to 590 | |
| 350 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 980 | |
| 480 to 970 |
| Tensile Strength: Yield (Proof), MPa | 480 to 850 | |
| 150 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 700 | |
| 220 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1040 |
| Melting Onset (Solidus), °C | 1410 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 430 |
| Thermal Conductivity, W/m-K | 24 | |
| 58 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 29 |
| Density, g/cm3 | 7.8 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.2 |
| Embodied Energy, MJ/kg | 41 | |
| 52 |
| Embodied Water, L/kg | 97 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 160 | |
| 27 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 1860 | |
| 100 to 2310 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 31 to 35 | |
| 16 to 32 |
| Strength to Weight: Bending, points | 26 to 28 | |
| 16 to 26 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 16 |
| Thermal Shock Resistance, points | 31 to 34 | |
| 17 to 34 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.020 | |
| 7.7 to 8.3 |
| Boron (B), % | 0 to 0.0015 | |
| 0 |
| Carbon (C), % | 0.17 to 0.23 | |
| 0 |
| Chromium (Cr), % | 10 to 11.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 89 to 90.5 |
| Iron (Fe), % | 84.5 to 88.3 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.015 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 0 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 1.8 to 2.2 |
| Niobium (Nb), % | 0.25 to 0.55 | |
| 0 |
| Nitrogen (N), % | 0.050 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |