MakeItFrom.com
Menu (ESC)

EN 1.4923 Stainless Steel vs. AWS BNi-5

EN 1.4923 stainless steel belongs to the iron alloys classification, while AWS BNi-5 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is EN 1.4923 stainless steel and the bottom bar is AWS BNi-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 870 to 980
470

Thermal Properties

Latent Heat of Fusion, J/g 270
470
Melting Completion (Liquidus), °C 1450
1140
Melting Onset (Solidus), °C 1410
1080
Specific Heat Capacity, J/kg-K 480
510
Thermal Expansion, µm/m-K 11
12

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
55
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.9
8.9
Embodied Energy, MJ/kg 41
130
Embodied Water, L/kg 100
260

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31 to 35
17
Strength to Weight: Bending, points 26 to 28
17
Thermal Shock Resistance, points 30 to 34
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
0 to 0.030
Carbon (C), % 0.18 to 0.24
0 to 0.060
Chromium (Cr), % 11 to 12.5
18.5 to 19.5
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 83.5 to 87.1
0
Manganese (Mn), % 0.4 to 0.9
0
Molybdenum (Mo), % 0.8 to 1.2
0
Nickel (Ni), % 0.3 to 0.8
69.1 to 71.8
Phosphorus (P), % 0 to 0.025
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 0.5
9.8 to 10.5
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0.25 to 0.35
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5