EN 1.4941 Stainless Steel vs. Grade 365 Molybdenum

EN 1.4941 stainless steel belongs to the iron alloys classification, while grade 365 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.4941 stainless steel and the bottom bar is grade 365 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
310
Elongation at Break, % 39
6.3
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 77
120
Tensile Strength: Ultimate (UTS), MPa 590
620
Tensile Strength: Yield (Proof), MPa 210
530

Thermal Properties

Latent Heat of Fusion, J/g 290
370
Specific Heat Capacity, J/kg-K 480
250
Thermal Expansion, µm/m-K 16
7.0

Otherwise Unclassified Properties

Density, g/cm3 7.8
10
Embodied Carbon, kg CO2/kg material 3.3
28
Embodied Energy, MJ/kg 47
330
Embodied Water, L/kg 140
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
37
Resilience: Unit (Modulus of Resilience), kJ/m3 110
450
Stiffness to Weight: Axial, points 14
17
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
16
Thermal Shock Resistance, points 13
21

Alloy Composition

Boron (B), % 0.0015 to 0.0050
0
Carbon (C), % 0.040 to 0.080
0 to 0.010
Chromium (Cr), % 17 to 19
0
Iron (Fe), % 65.1 to 73.6
0 to 0.010
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0
99.9 to 100
Nickel (Ni), % 9.0 to 12
0 to 0.0020
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0 to 0.010
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0.4 to 0.8
0