EN 1.4945 Stainless Steel vs. Grade 361 Molybdenum
EN 1.4945 stainless steel belongs to the iron alloys classification, while grade 361 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is EN 1.4945 stainless steel and the bottom bar is grade 361 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 310 |
| Elongation at Break, % | 19 to 34 | |
| 6.3 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 740 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 290 to 550 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 250 |
| Thermal Expansion, µm/m-K | 17 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 5.0 | |
| 28 |
| Embodied Energy, MJ/kg | 73 | |
| 330 |
| Embodied Water, L/kg | 150 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 180 | |
| 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 760 | |
| 450 |
| Stiffness to Weight: Axial, points | 14 | |
| 17 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 17 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 16 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0.040 to 0.1 | |
| 0 to 0.010 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 0 |
| Iron (Fe), % | 57.9 to 65.7 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 99.9 to 100 |
| Nickel (Ni), % | 15.5 to 17.5 | |
| 0 to 0.0050 |
| Niobium (Nb), % | 0.4 to 1.2 | |
| 0 |
| Nitrogen (N), % | 0.060 to 0.14 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0070 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tungsten (W), % | 2.5 to 3.5 | |
| 0 |