EN 1.4951 Stainless Steel vs. AISI 430F Stainless Steel

Both EN 1.4951 stainless steel and AISI 430F stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is AISI 430F stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
230
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
23
Fatigue Strength, MPa 190
210
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
77
Shear Strength, MPa 430
340
Tensile Strength: Ultimate (UTS), MPa 630
540
Tensile Strength: Yield (Proof), MPa 220
310

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1360
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
8.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
2.1
Embodied Energy, MJ/kg 61
29
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 26
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 130
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 3.9
6.7
Thermal Shock Resistance, points 14
19

Alloy Composition

Carbon (C), % 0.040 to 0.080
0 to 0.12
Chromium (Cr), % 24 to 26
16 to 18
Iron (Fe), % 49.1 to 57
79.2 to 83.9
Manganese (Mn), % 0 to 2.0
0 to 1.3
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.035
0 to 0.060
Silicon (Si), % 0 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.015
0.15 to 0.35