EN 1.4951 Stainless Steel vs. AWS ER80S-B6

Both EN 1.4951 stainless steel and AWS ER80S-B6 are iron alloys. They have 59% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is AWS ER80S-B6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
19
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
74
Tensile Strength: Ultimate (UTS), MPa 630
620
Tensile Strength: Yield (Proof), MPa 220
540

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
4.7
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.8
Embodied Energy, MJ/kg 61
24
Embodied Water, L/kg 190
71

Common Calculations

PREN (Pitting Resistance) 26
7.1
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 130
750
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
22
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 3.9
11
Thermal Shock Resistance, points 14
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.040 to 0.080
0 to 0.1
Chromium (Cr), % 24 to 26
4.5 to 6.0
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 49.1 to 57
90.6 to 94.7
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 19 to 22
0 to 0.6
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.025
Residuals, % 0
0 to 0.5