EN 1.4951 Stainless Steel vs. EN 1.4035 Stainless Steel

Both EN 1.4951 stainless steel and EN 1.4035 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is EN 1.4035 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
220
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
18
Fatigue Strength, MPa 190
250
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
76
Shear Strength, MPa 430
430
Tensile Strength: Ultimate (UTS), MPa 630
690
Tensile Strength: Yield (Proof), MPa 220
400

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 450
380
Maximum Temperature: Mechanical, °C 1100
760
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1360
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
29
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
7.0
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
2.0
Embodied Energy, MJ/kg 61
27
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 26
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 130
420
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
25
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 3.9
7.8
Thermal Shock Resistance, points 14
25

Alloy Composition

Carbon (C), % 0.040 to 0.080
0.43 to 0.5
Chromium (Cr), % 24 to 26
12.5 to 14
Iron (Fe), % 49.1 to 57
82.1 to 86.9
Manganese (Mn), % 0 to 2.0
0 to 2.0
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.015
0.15 to 0.35