EN 1.4951 Stainless Steel vs. EN 1.4113 Stainless Steel

Both EN 1.4951 stainless steel and EN 1.4113 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is EN 1.4113 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
20
Fatigue Strength, MPa 190
200
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
78
Shear Strength, MPa 430
340
Tensile Strength: Ultimate (UTS), MPa 630
540
Tensile Strength: Yield (Proof), MPa 220
310

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
880
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
2.4
Embodied Energy, MJ/kg 61
33
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 26
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
94
Resilience: Unit (Modulus of Resilience), kJ/m3 130
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 3.9
6.7
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0.040 to 0.080
0 to 0.080
Chromium (Cr), % 24 to 26
16 to 18
Iron (Fe), % 49.1 to 57
78.5 to 83.1
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0.9 to 1.4
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015