EN 1.4951 Stainless Steel vs. EN 1.4405 Stainless Steel

Both EN 1.4951 stainless steel and EN 1.4405 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
17
Fatigue Strength, MPa 190
370
Impact Strength: V-Notched Charpy, J 98
68
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 630
860
Tensile Strength: Yield (Proof), MPa 220
610

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
13
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
2.8
Embodied Energy, MJ/kg 61
39
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 26
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
130
Resilience: Unit (Modulus of Resilience), kJ/m3 130
950
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
31
Strength to Weight: Bending, points 21
26
Thermal Diffusivity, mm2/s 3.9
4.6
Thermal Shock Resistance, points 14
29

Alloy Composition

Carbon (C), % 0.040 to 0.080
0 to 0.060
Chromium (Cr), % 24 to 26
15 to 17
Iron (Fe), % 49.1 to 57
73.6 to 80.3
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0.7 to 1.5
Nickel (Ni), % 19 to 22
4.0 to 6.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 0.7
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.025