EN 1.4951 Stainless Steel vs. EN 1.4469 Stainless Steel

Both EN 1.4951 stainless steel and EN 1.4469 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is EN 1.4469 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 38
25
Fatigue Strength, MPa 190
380
Impact Strength: V-Notched Charpy, J 98
56
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 79
81
Tensile Strength: Ultimate (UTS), MPa 630
740
Tensile Strength: Yield (Proof), MPa 220
550

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
21
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
4.1
Embodied Energy, MJ/kg 61
57
Embodied Water, L/kg 190
180

Common Calculations

PREN (Pitting Resistance) 26
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
170
Resilience: Unit (Modulus of Resilience), kJ/m3 130
730
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
26
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 3.9
4.6
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0.040 to 0.080
0 to 0.030
Chromium (Cr), % 24 to 26
25 to 27
Copper (Cu), % 0
0 to 1.3
Iron (Fe), % 49.1 to 57
56.4 to 65.9
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 5.0
Nickel (Ni), % 19 to 22
6.0 to 8.0
Nitrogen (N), % 0 to 0.1
0.12 to 0.22
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.025