EN 1.4951 Stainless Steel vs. EN 1.4825 Stainless Steel

Both EN 1.4951 stainless steel and EN 1.4825 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is EN 1.4825 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
17
Fatigue Strength, MPa 190
160
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 630
510
Tensile Strength: Yield (Proof), MPa 220
260

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
900
Melting Completion (Liquidus), °C 1410
1410
Melting Onset (Solidus), °C 1360
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 25
15
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
3.1
Embodied Energy, MJ/kg 61
43
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 26
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
72
Resilience: Unit (Modulus of Resilience), kJ/m3 130
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 3.9
4.0
Thermal Shock Resistance, points 14
12

Alloy Composition

Carbon (C), % 0.040 to 0.080
0.15 to 0.35
Chromium (Cr), % 24 to 26
17 to 19
Iron (Fe), % 49.1 to 57
65.6 to 74.4
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 19 to 22
8.0 to 10
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.7
0.5 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.030