EN 1.4951 Stainless Steel vs. EN 1.7336 Steel

Both EN 1.4951 stainless steel and EN 1.7336 steel are iron alloys. They have 55% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is EN 1.7336 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
22
Fatigue Strength, MPa 190
240 to 310
Impact Strength: V-Notched Charpy, J 98
39 to 46
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 430
370
Tensile Strength: Ultimate (UTS), MPa 630
590
Tensile Strength: Yield (Proof), MPa 220
340 to 440

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
430
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 25
3.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.6
Embodied Energy, MJ/kg 61
21
Embodied Water, L/kg 190
53

Common Calculations

PREN (Pitting Resistance) 26
3.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 130
310 to 510
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.9
11
Thermal Shock Resistance, points 14
17

Alloy Composition

Carbon (C), % 0.040 to 0.080
0 to 0.17
Chromium (Cr), % 24 to 26
1.0 to 1.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 49.1 to 57
95.6 to 97.7
Manganese (Mn), % 0 to 2.0
0.4 to 0.65
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 19 to 22
0 to 0.3
Nitrogen (N), % 0 to 0.1
0 to 0.012
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 0 to 0.7
0.5 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.0050