EN 1.4951 Stainless Steel vs. S82012 Stainless Steel

Both EN 1.4951 stainless steel and S82012 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is S82012 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
40
Fatigue Strength, MPa 190
480
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
78
Shear Strength, MPa 430
550
Tensile Strength: Ultimate (UTS), MPa 630
800
Tensile Strength: Yield (Proof), MPa 220
560

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
950
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
11
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
2.4
Embodied Energy, MJ/kg 61
35
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 26
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
290
Resilience: Unit (Modulus of Resilience), kJ/m3 130
790
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
29
Strength to Weight: Bending, points 21
25
Thermal Diffusivity, mm2/s 3.9
3.9
Thermal Shock Resistance, points 14
23

Alloy Composition

Carbon (C), % 0.040 to 0.080
0 to 0.050
Chromium (Cr), % 24 to 26
19 to 20.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 49.1 to 57
71.3 to 77.9
Manganese (Mn), % 0 to 2.0
2.0 to 4.0
Molybdenum (Mo), % 0
0.1 to 0.6
Nickel (Ni), % 19 to 22
0.8 to 1.5
Nitrogen (N), % 0 to 0.1
0.16 to 0.26
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.7
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.0050