EN 1.4962 Stainless Steel vs. ASTM A588 Steel

Both EN 1.4962 stainless steel and ASTM A588 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4962 stainless steel and the bottom bar is ASTM A588 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 210
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 22 to 34
22
Fatigue Strength, MPa 210 to 330
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 420 to 440
350
Tensile Strength: Ultimate (UTS), MPa 630 to 690
550
Tensile Strength: Yield (Proof), MPa 260 to 490
390

Thermal Properties

Latent Heat of Fusion, J/g 280
250 to 260
Maximum Temperature: Mechanical, °C 910
410
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1440
1410 to 1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
43 to 44
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 23
2.3 to 2.5
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 4.1
1.5 to 1.6
Embodied Energy, MJ/kg 59
20 to 22
Embodied Water, L/kg 150
50 to 51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 170
110
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 610
400
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 24
20
Strength to Weight: Bending, points 20 to 21
19
Thermal Diffusivity, mm2/s 3.7
12
Thermal Shock Resistance, points 14 to 16
16