EN 1.4971 Stainless Steel vs. EN 1.0455 Cast Steel

Both EN 1.4971 stainless steel and EN 1.0455 cast steel are iron alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4971 stainless steel and the bottom bar is EN 1.0455 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 34
25
Fatigue Strength, MPa 270
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 800
530
Tensile Strength: Yield (Proof), MPa 340
270

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 70
1.8
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 7.6
1.4
Embodied Energy, MJ/kg 110
18
Embodied Water, L/kg 300
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110
Resilience: Unit (Modulus of Resilience), kJ/m3 280
190
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26
19
Strength to Weight: Bending, points 23
18
Thermal Diffusivity, mm2/s 3.4
14
Thermal Shock Resistance, points 19
17

Alloy Composition

Carbon (C), % 0.080 to 0.16
0 to 0.23
Chromium (Cr), % 20 to 22.5
0
Cobalt (Co), % 18.5 to 21
0
Iron (Fe), % 24.3 to 37.1
97.9 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.2
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 19 to 21
0
Niobium (Nb), % 0.75 to 1.3
0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.025
Tungsten (W), % 2.0 to 3.0
0