EN 1.5024 steel belongs to the iron alloys classification, while AWS BNi-2 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.5024 steel and the bottom bar is AWS BNi-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
180
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 72
68
Tensile Strength: Ultimate (UTS), MPa 670 to 1930
440

Thermal Properties

Latent Heat of Fusion, J/g 270
360
Melting Completion (Liquidus), °C 1440
1000
Melting Onset (Solidus), °C 1400
970
Specific Heat Capacity, J/kg-K 480
490
Thermal Expansion, µm/m-K 13
11

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
55
Density, g/cm3 7.7
8.2
Embodied Carbon, kg CO2/kg material 1.4
9.3
Embodied Energy, MJ/kg 19
130
Embodied Water, L/kg 45
230

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 24 to 69
15
Strength to Weight: Bending, points 22 to 45
16
Thermal Shock Resistance, points 20 to 58
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
2.8 to 3.5
Carbon (C), % 0.42 to 0.5
0 to 0.060
Chromium (Cr), % 0
6.0 to 8.0
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 96.7 to 97.6
2.5 to 3.5
Manganese (Mn), % 0.5 to 0.8
0
Nickel (Ni), % 0
79.1 to 84.8
Phosphorus (P), % 0 to 0.025
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 1.5 to 2.0
4.0 to 5.0
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5