EN 1.5026 Steel vs. C91300 Bell Metal
EN 1.5026 steel belongs to the iron alloys classification, while C91300 bell metal belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.5026 steel and the bottom bar is C91300 bell metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 1980 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 150 |
| Melting Completion (Liquidus), °C | 1440 | |
| 890 |
| Melting Onset (Solidus), °C | 1390 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 360 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 7.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 39 |
| Density, g/cm3 | 7.7 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 4.5 |
| Embodied Energy, MJ/kg | 19 | |
| 74 |
| Embodied Water, L/kg | 46 | |
| 460 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 6.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 24 to 71 | |
| 7.8 |
| Strength to Weight: Bending, points | 22 to 45 | |
| 10 |
| Thermal Shock Resistance, points | 20 to 60 | |
| 9.3 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0.52 to 0.6 | |
| 0 |
| Copper (Cu), % | 0 | |
| 79 to 82 |
| Iron (Fe), % | 96.5 to 97.3 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 1.5 |
| Silicon (Si), % | 1.6 to 2.0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 18 to 20 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.6 |