EN 1.5113 Steel vs. N07041 Nickel
EN 1.5113 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.5113 steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 11 to 18 | |
| 14 |
| Fatigue Strength, MPa | 220 to 470 | |
| 540 |
| Shear Strength, MPa | 360 to 540 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 900 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 320 to 770 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1410 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 52 | |
| 11 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 96 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 1570 | |
| 2510 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 32 | |
| 47 |
| Strength to Weight: Bending, points | 20 to 27 | |
| 34 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.0 |
| Thermal Shock Resistance, points | 17 to 26 | |
| 38 |