EN 1.5503 Steel vs. S17400 Stainless Steel

Both EN 1.5503 steel and S17400 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.5503 steel and the bottom bar is S17400 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120 to 160
280 to 440
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 17
11 to 21
Fatigue Strength, MPa 180 to 280
380 to 670
Poisson's Ratio 0.29
0.28
Reduction in Area, % 63 to 72
40 to 62
Shear Modulus, GPa 73
75
Shear Strength, MPa 270 to 320
570 to 830
Tensile Strength: Ultimate (UTS), MPa 400 to 520
910 to 1390
Tensile Strength: Yield (Proof), MPa 270 to 430
580 to 1250

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
850
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
14
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.7
Embodied Energy, MJ/kg 18
39
Embodied Water, L/kg 46
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 41 to 81
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 490
880 to 4060
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 14 to 19
32 to 49
Strength to Weight: Bending, points 15 to 18
27 to 35
Thermal Diffusivity, mm2/s 14
4.5
Thermal Shock Resistance, points 12 to 15
30 to 46

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.16 to 0.2
0 to 0.070
Chromium (Cr), % 0
15 to 17
Copper (Cu), % 0 to 0.25
3.0 to 5.0
Iron (Fe), % 98.4 to 99.239
70.4 to 78.9
Manganese (Mn), % 0.6 to 0.8
0 to 1.0
Nickel (Ni), % 0
3.0 to 5.0
Niobium (Nb), % 0
0.15 to 0.45
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030