EN 1.5520 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.5520 steel and the bottom bar is N07041 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 11 to 21
14
Fatigue Strength, MPa 210 to 300
540
Shear Strength, MPa 290 to 340
850
Tensile Strength: Ultimate (UTS), MPa 410 to 1410
1400
Tensile Strength: Yield (Proof), MPa 300 to 480
1050

Thermal Properties

Melting Onset (Solidus), °C 1420
1320
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 50
11
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.2

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 42 to 230
180
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 600
2510
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15 to 50
47
Strength to Weight: Bending, points 16 to 36
34
Thermal Diffusivity, mm2/s 13
3.0
Thermal Shock Resistance, points 12 to 41
38