EN 1.5521 Steel vs. EN 1.8836 Steel

Both EN 1.5521 steel and EN 1.8836 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.5521 steel and the bottom bar is EN 1.8836 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 180
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 21
21
Fatigue Strength, MPa 210 to 310
290
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 310 to 360
360
Tensile Strength: Ultimate (UTS), MPa 430 to 1390
570
Tensile Strength: Yield (Proof), MPa 300 to 490
410

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 47
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 44 to 230
110
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 630
450
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15 to 49
20
Strength to Weight: Bending, points 16 to 35
19
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 13 to 41
17

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.054
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.16 to 0.2
0 to 0.18
Chromium (Cr), % 0
0 to 0.35
Copper (Cu), % 0 to 0.25
0 to 0.6
Iron (Fe), % 98 to 98.9
95.1 to 99.985
Manganese (Mn), % 0.9 to 1.2
0 to 1.8
Molybdenum (Mo), % 0
0 to 0.23
Nickel (Ni), % 0
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.3
0 to 0.55
Sulfur (S), % 0 to 0.025
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.14