EN 1.5521 Steel vs. EN 1.8891 Steel

Both EN 1.5521 steel and EN 1.8891 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.5521 steel and the bottom bar is EN 1.8891 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 180
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 21
19
Fatigue Strength, MPa 210 to 310
330
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 310 to 360
380
Tensile Strength: Ultimate (UTS), MPa 430 to 1390
610
Tensile Strength: Yield (Proof), MPa 300 to 490
480

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 19
24
Embodied Water, L/kg 47
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 44 to 230
110
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 630
630
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15 to 49
22
Strength to Weight: Bending, points 16 to 35
20
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 13 to 41
18

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.16 to 0.2
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0 to 0.25
0 to 0.7
Iron (Fe), % 98 to 98.9
95.2 to 99
Manganese (Mn), % 0.9 to 1.2
1.0 to 1.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.8
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.3
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.2