EN 1.5521 Steel vs. Solder Alloy 102

EN 1.5521 steel belongs to the iron alloys classification, while solder alloy 102 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.5521 steel and the bottom bar is solder alloy 102.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
38
Elongation at Break, % 11 to 21
48
Poisson's Ratio 0.29
0.39
Shear Modulus, GPa 73
14
Tensile Strength: Ultimate (UTS), MPa 430 to 1390
31

Thermal Properties

Latent Heat of Fusion, J/g 250
46
Melting Completion (Liquidus), °C 1460
180
Melting Onset (Solidus), °C 1420
180
Specific Heat Capacity, J/kg-K 470
190
Thermal Conductivity, W/m-K 51
53
Thermal Expansion, µm/m-K 13
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
12
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
13

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 1.4
11
Embodied Energy, MJ/kg 19
180
Embodied Water, L/kg 47
930

Common Calculations

Stiffness to Weight: Axial, points 13
2.4
Stiffness to Weight: Bending, points 24
13
Strength to Weight: Axial, points 15 to 49
1.0
Strength to Weight: Bending, points 16 to 35
2.5
Thermal Diffusivity, mm2/s 14
32
Thermal Shock Resistance, points 13 to 41
2.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.050
Boron (B), % 0.00080 to 0.0050
0
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.16 to 0.2
0
Copper (Cu), % 0 to 0.25
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 98 to 98.9
0 to 0.020
Lead (Pb), % 0
36 to 37.5
Manganese (Mn), % 0.9 to 1.2
0
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.3
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
62.5 to 63.5
Zinc (Zn), % 0
0 to 0.0010