EN 1.5521 Steel vs. Reactor Grade Zirconium
EN 1.5521 steel belongs to the iron alloys classification, while reactor grade zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.5521 steel and the bottom bar is reactor grade zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 11 to 21 | |
| 21 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 1390 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 300 to 490 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 51 | |
| 22 |
| Thermal Expansion, µm/m-K | 13 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.5 |
| Embodied Water, L/kg | 47 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 230 | |
| 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 630 | |
| 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 49 | |
| 14 |
| Strength to Weight: Bending, points | 16 to 35 | |
| 16 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 13 to 41 | |
| 41 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.16 to 0.2 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 98 to 98.9 | |
| 0 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 99.7 to 100 |
| Residuals, % | 0 | |
| 0 to 0.27 |