EN 1.5521 Steel vs. S42035 Stainless Steel

Both EN 1.5521 steel and S42035 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.5521 steel and the bottom bar is S42035 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 180
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 21
18
Fatigue Strength, MPa 210 to 310
260
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 310 to 360
390
Tensile Strength: Ultimate (UTS), MPa 430 to 1390
630
Tensile Strength: Yield (Proof), MPa 300 to 490
430

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
810
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
27
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
9.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.4
Embodied Energy, MJ/kg 19
34
Embodied Water, L/kg 47
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 44 to 230
100
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 630
460
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15 to 49
22
Strength to Weight: Bending, points 16 to 35
21
Thermal Diffusivity, mm2/s 14
7.2
Thermal Shock Resistance, points 13 to 41
22

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.16 to 0.2
0 to 0.080
Chromium (Cr), % 0
13.5 to 15.5
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 98 to 98.9
78.1 to 85
Manganese (Mn), % 0.9 to 1.2
0 to 1.0
Molybdenum (Mo), % 0
0.2 to 1.2
Nickel (Ni), % 0
1.0 to 2.5
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Titanium (Ti), % 0
0.3 to 0.5