EN 1.5521 Steel vs. ZA-12

EN 1.5521 steel belongs to the iron alloys classification, while ZA-12 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.5521 steel and the bottom bar is ZA-12.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 180
89 to 100
Elastic (Young's, Tensile) Modulus, GPa 190
83
Elongation at Break, % 11 to 21
1.6 to 5.3
Fatigue Strength, MPa 210 to 310
73 to 120
Poisson's Ratio 0.29
0.26
Shear Modulus, GPa 73
33
Shear Strength, MPa 310 to 360
240 to 300
Tensile Strength: Ultimate (UTS), MPa 430 to 1390
260 to 400
Tensile Strength: Yield (Proof), MPa 300 to 490
210 to 320

Thermal Properties

Latent Heat of Fusion, J/g 250
120
Maximum Temperature: Mechanical, °C 400
100
Melting Completion (Liquidus), °C 1460
430
Melting Onset (Solidus), °C 1420
380
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 51
120
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
28
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
42

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
11
Density, g/cm3 7.8
6.0
Embodied Carbon, kg CO2/kg material 1.4
3.4
Embodied Energy, MJ/kg 19
64
Embodied Water, L/kg 47
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 44 to 230
4.0 to 20
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 630
260 to 620
Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15 to 49
12 to 19
Strength to Weight: Bending, points 16 to 35
15 to 20
Thermal Diffusivity, mm2/s 14
43
Thermal Shock Resistance, points 13 to 41
9.4 to 14

Alloy Composition

Aluminum (Al), % 0
10.5 to 11.5
Boron (B), % 0.00080 to 0.0050
0
Cadmium (Cd), % 0
0 to 0.0060
Carbon (C), % 0.16 to 0.2
0
Copper (Cu), % 0 to 0.25
0.5 to 1.2
Iron (Fe), % 98 to 98.9
0 to 0.075
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 0
0.015 to 0.030
Manganese (Mn), % 0.9 to 1.2
0
Nickel (Ni), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.3
0 to 0.060
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
87.1 to 89