EN 1.5918 Steel vs. N06110 Nickel

EN 1.5918 steel belongs to the iron alloys classification, while N06110 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.5918 steel and the bottom bar is N06110 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
84
Tensile Strength: Ultimate (UTS), MPa 530 to 1390
730

Thermal Properties

Latent Heat of Fusion, J/g 250
340
Maximum Temperature: Mechanical, °C 440
1020
Melting Completion (Liquidus), °C 1460
1490
Melting Onset (Solidus), °C 1420
1440
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
65
Density, g/cm3 7.9
8.6
Embodied Carbon, kg CO2/kg material 1.6
11
Embodied Energy, MJ/kg 21
160
Embodied Water, L/kg 56
320

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19 to 49
23
Strength to Weight: Bending, points 18 to 35
21
Thermal Shock Resistance, points 15 to 41
20

Alloy Composition

Aluminum (Al), % 0
0 to 1.0
Carbon (C), % 0.14 to 0.2
0 to 0.15
Chromium (Cr), % 1.4 to 1.7
28 to 33
Copper (Cu), % 0 to 0.25
0 to 0.5
Iron (Fe), % 94.9 to 96.6
0 to 1.0
Manganese (Mn), % 0.5 to 0.9
0 to 1.0
Molybdenum (Mo), % 0
9.0 to 12
Nickel (Ni), % 1.4 to 1.7
51 to 62
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.5
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0 to 1.0
Tungsten (W), % 0
1.0 to 4.0