EN 1.6220 Steel vs. ASTM A204 Steel

Both EN 1.6220 steel and ASTM A204 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.6220 steel and the bottom bar is ASTM A204 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23 to 25
18 to 22
Fatigue Strength, MPa 240 to 250
200 to 220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 550 to 580
520 to 590
Tensile Strength: Yield (Proof), MPa 340
290 to 330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420 to 1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 48
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
90 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 300 to 310
220 to 290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 20
18 to 21
Strength to Weight: Bending, points 19 to 20
18 to 20
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 16 to 17
15 to 17