EN 1.6553 Steel vs. EN 1.7335 Steel

Both EN 1.6553 steel and EN 1.7335 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.6553 steel and the bottom bar is EN 1.7335 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 240
150 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19 to 21
21 to 22
Fatigue Strength, MPa 330 to 460
200 to 220
Impact Strength: V-Notched Charpy, J 30
31 to 35
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 710 to 800
500 to 520
Tensile Strength: Yield (Proof), MPa 470 to 670
280 to 310

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
430
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.7
2.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
1.6
Embodied Energy, MJ/kg 21
21
Embodied Water, L/kg 51
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 150
91 to 97
Resilience: Unit (Modulus of Resilience), kJ/m3 600 to 1190
210 to 260
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
18
Strength to Weight: Bending, points 23 to 24
18
Thermal Diffusivity, mm2/s 10
12
Thermal Shock Resistance, points 21 to 23
15

Alloy Composition

Carbon (C), % 0.23 to 0.28
0.080 to 0.18
Chromium (Cr), % 0.4 to 0.8
0.7 to 1.2
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 95.6 to 98.2
96.4 to 98.4
Manganese (Mn), % 0.6 to 1.0
0.4 to 1.0
Molybdenum (Mo), % 0.15 to 0.3
0.4 to 0.6
Nickel (Ni), % 0.4 to 0.8
0
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.8
0 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.010
Vanadium (V), % 0 to 0.030
0