Both EN 1.6563 steel and ASTM A514 steel are iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.6563 steel and the bottom bar is ASTM A514 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 620 to 1850
790 to 830

Thermal Properties

Latent Heat of Fusion, J/g 250
250 to 260
Maximum Temperature: Mechanical, °C 420
400 to 440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
37 to 51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.2 to 7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.3 to 8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 3.6
2.3 to 3.8
Density, g/cm3 7.9
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 1.7
1.6 to 1.8
Embodied Energy, MJ/kg 22
21 to 25
Embodied Water, L/kg 54
48 to 57

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22 to 65
28 to 29
Strength to Weight: Bending, points 21 to 43
24 to 25
Thermal Diffusivity, mm2/s 12
10 to 14
Thermal Shock Resistance, points 18 to 54
23 to 24