EN 1.6570 Steel vs. SAE-AISI 1548 Steel

Both EN 1.6570 steel and SAE-AISI 1548 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.6570 steel and the bottom bar is SAE-AISI 1548 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270 to 340
220 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
11 to 16
Fatigue Strength, MPa 500 to 660
270 to 430
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Tensile Strength: Ultimate (UTS), MPa 910 to 1130
730 to 830
Tensile Strength: Yield (Proof), MPa 760 to 1060
420 to 690

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 440
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.9
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
19
Embodied Water, L/kg 56
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 140
79 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 1520 to 3010
470 to 1280
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 32 to 40
26 to 30
Strength to Weight: Bending, points 27 to 31
23 to 25
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 27 to 33
23 to 27

Alloy Composition

Carbon (C), % 0.28 to 0.35
0.44 to 0.52
Chromium (Cr), % 1.0 to 1.4
0
Iron (Fe), % 94 to 96.2
98 to 98.5
Manganese (Mn), % 0.6 to 1.0
1.1 to 1.4
Molybdenum (Mo), % 0.3 to 0.5
0
Nickel (Ni), % 1.6 to 2.1
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.6
0
Sulfur (S), % 0 to 0.015
0 to 0.050

Comparable Variants