EN 1.6582 Steel vs. S15700 Stainless Steel

Both EN 1.6582 steel and S15700 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.6582 steel and the bottom bar is S15700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 300
200 to 460
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 620 to 1750
1180 to 1890

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 440
870
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 3.6
15
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
3.4
Embodied Energy, MJ/kg 22
47
Embodied Water, L/kg 56
140

Common Calculations

PREN (Pitting Resistance) 2.2
23
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22 to 62
42 to 67
Strength to Weight: Bending, points 21 to 41
32 to 43
Thermal Diffusivity, mm2/s 11
4.2
Thermal Shock Resistance, points 18 to 51
39 to 63

Alloy Composition

Aluminum (Al), % 0
0.75 to 1.5
Carbon (C), % 0.3 to 0.38
0 to 0.090
Chromium (Cr), % 1.3 to 1.7
14 to 16
Iron (Fe), % 94.7 to 96.5
69.6 to 76.8
Manganese (Mn), % 0.5 to 0.8
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.3
2.0 to 3.0
Nickel (Ni), % 1.3 to 1.7
6.5 to 7.7
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.030

Comparable Variants