EN 1.6958 Steel vs. AISI 308 Stainless Steel

Both EN 1.6958 steel and AISI 308 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.6958 steel and the bottom bar is AISI 308 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 340
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16
45
Fatigue Strength, MPa 700
210
Poisson's Ratio 0.29
0.28
Reduction in Area, % 56
57
Shear Modulus, GPa 73
78
Shear Strength, MPa 700
410
Tensile Strength: Ultimate (UTS), MPa 1140
590
Tensile Strength: Yield (Proof), MPa 1070
230

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 450
990
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 47
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.9
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 9.1
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 5.0
17
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.0
3.2
Embodied Energy, MJ/kg 27
46
Embodied Water, L/kg 60
150

Common Calculations

PREN (Pitting Resistance) 2.9
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
210
Resilience: Unit (Modulus of Resilience), kJ/m3 3050
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 40
21
Strength to Weight: Bending, points 31
20
Thermal Diffusivity, mm2/s 13
4.1
Thermal Shock Resistance, points 39
13

Alloy Composition

Aluminum (Al), % 0.0050 to 0.050
0
Carbon (C), % 0.25 to 0.3
0 to 0.080
Chromium (Cr), % 1.2 to 1.7
19 to 21
Iron (Fe), % 92.6 to 94.5
64.1 to 71
Manganese (Mn), % 0.2 to 0.5
0 to 2.0
Molybdenum (Mo), % 0.35 to 0.55
0
Nickel (Ni), % 3.3 to 3.8
10 to 12
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0.15 to 0.3
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030
Vanadium (V), % 0 to 0.12
0