EN 1.6958 Steel vs. EN 1.7076 Steel

Both EN 1.6958 steel and EN 1.7076 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.6958 steel and the bottom bar is EN 1.7076 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 340
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Reduction in Area, % 56
64 to 69
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 1140
470 to 1700

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 450
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 47
45
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.9
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.1
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 5.0
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.0
1.4
Embodied Energy, MJ/kg 27
19
Embodied Water, L/kg 60
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 40
17 to 60
Strength to Weight: Bending, points 31
17 to 40
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 39
14 to 50

Alloy Composition

Aluminum (Al), % 0.0050 to 0.050
0
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.25 to 0.3
0.3 to 0.34
Chromium (Cr), % 1.2 to 1.7
0.9 to 1.2
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 92.6 to 94.5
97 to 98.2
Manganese (Mn), % 0.2 to 0.5
0.6 to 0.9
Molybdenum (Mo), % 0.35 to 0.55
0
Nickel (Ni), % 3.3 to 3.8
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.3
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025
Vanadium (V), % 0 to 0.12
0